321H stainless steel plate

321H Stainless Steel Sheet for Sale

Chemical Composition (%) of 321H Stainless Steel Plate
Carbon Silicon Sulfur Phosphorus Chromium Titanium Manganese Nickel Nitrogen
0.04-0.14 0.75 0.03 0.045 17.0-19.0 4 x (C + N) min.-0.70 max. 2.00 9.0-12.0 0.10
Mechanical Properties of 321H Stainless Steel Plate
Yield Strengtd
0.2% Offset
Ultimate Tensile
Strength
Elongation
in 2 in.
Hardness
psi (min.) (MPa) psi (min.) (MPa) % (min.) (max.)
30,000 205 75,000 515 40 217 Brinell
Physical Properties of 321H Stainless Steel Plate
Density lb/inᶟ 0.286
Density g/cmᶟ 7.920
Melting Range 2550-2635°F/1398 – 1446 °C
Thermal Conductivity at 212°F (100°C) 9.3 BTU/hr/ft²/ft/°F
Thermal Conductivity at 212°F (100°C) 16.0 W/m-°K
Electrical Resistivity 72 Microhm-cm at 20°C

Alloy 321 (UNS S32100) is titanium stabilized austenitic stainless steel plate with good general corrosion resistance. It has excellent resistance to intergranular corrosion after exposure to temperatures in the chromium carbide precipitation range of 800 - 1500°F (427 - 816°C). The alloy resists oxidation to 1500°F (816°C) and has higher creep and stress rupture properties than alloys 304 and 304L. It also possesses good low temperature toughness.

Alloy 321H (UNS S 32109) stainless steel plate is the higher carbon (0.04 - 0.10) version of the alloy. It was developed for enhanced creep resistance and for higher strength at temperatures above 1000oF (537°C). In most instances, the carbon content of the plate enables dual certification.

Alloy 321 stainless steel plate cannot be hardened by heat treatment, only by cold working. It can be easily welded and processed by standard shop fabrication practices.