416HT stainless steel

Chemical Composition (%) of 416HT Stainless Steel Plate

C	Mn	Si	P	S	Cr
0.15	1.25	1.00	0.06	0.15	12.0-14.0

Mechanical Properties of 416HT Stainless Steel Plate

Tempering Temperature (°C)	Tensile Strength (MPa)	Yield Strength 0.2% Proof (MPa)	Elongation (% in 50mm)	Hardness Brinell (HB)	Impact Charpy V (J)
Annealed *	517	276	30	262	–
Condition T **	758	586	18	248-302	–
204	1340	1050	11	388	20
316	1350	1060	12	388	22
427	1405	1110	11	401	#
538	1000	795	13	321	#
593	840	705	19	248	27
650	750	575	20	223	38
* Annealed properties are typical for Condition A of ASTM A582.
** Hardened and tempered Condition T of ASTM A582 – Brinell Hardness is specified range, other properties are typical only.
# Due to associated low impact resistance this steel should not be tempered in the range 400-

Physical Properties of 416HT Stainless Steel Plate

Density kg /m³	Thermal Conductivity W/mK	Electrical Resistivity (Microhm/cm)	Modulus of Elasticity	Coefficient of Thermal Expansion µm/m/°C	Specific Heat (J/kg.K)	Specific Gravity
7750	24.9at 212°F	43 at 68°F	200 GPa	9.9 at 32 – 212°F	460 at 32°F to 212°F	7.7

Type 416HT Stainless Steel is a stainless steel which is martensitic and has been hardened by heat treatment to higher strength and hardness levels. It has much better machining properties than the austenitic grades, but lower corrosion resistance.It has the highest machinability of any stainless steel at about 85% of that of a free-machining carbon steel. Martensitic stainless steels were designed to be hardenable by heat treatment and also corrosion resistant.

Although Alloy 416HT and other martensitic stainless steels are not as resistant as austenitic or ferritic stainless, it still demonstrates good corrosion and oxidation resistance plus high strength in the hardened and tempered condition. Alloy 416HT is easily machined, is always magnetic, and has low frictional properties that reduce galling and seizing.