Steel Plate EN10025-2

HOME > steel grades
EN10025-2 S235J0
Chemical composition % MAX
THICKNESS(MM) C Mn Si P S N Cu
≦40 0.17 1.4 ~ 0.03 0.03 0.012 0.55
>40 0.17
Mechanical properties MIN
  Yield Strength MPa Tensile Strength MPa Elongation in 2 in. %
≦16 235 360-510 17
>16,  ≦100 225
>100 175 340-500
EN10025-2 S235JR
Chemical composition % MAX
THICKNESS(MM) C Mn Si P S N Cu
≦40 0.17 1.4 ~ 0.035 0.035 0.012 0.55
>40 0.20
Mechanical properties MIN
  Yield Strength MPa Tensile Strength MPa Elongation in 2 in. %
≦16 235 360-510 17
>16,  ≦100 215
>100 175 340-500
EN10025-2 S275JR
Chemical composition % MAX
THICKNESS(MM) C Mn Si P S N Cu
≦40 0.21 1.5 ~ 0.035 0.035 0.012 0.55
>40 0.22
Mechanical properties MIN
  Yield Strength MPa Tensile Strength MPa Elongation in 2 in. %
≦16 275 410-580 15
>16,  ≦100 235
>100 205 380-540
EN10025-2 S235J2
Chemical composition % MAX
THICKNESS(MM) C Mn Si P S N Cu
≦40 0.17 1.4 ~ 0.025 0.025 ~ 0.55
>40 0.17
Mechanical properties MIN
  Yield Strength MPa Tensile Strength MPa Elongation in 2 in. %
≦16 235 360-510 15
>16,  ≦100 225
>100 165 330-510
EN10025-2 S275J2
Chemical composition % MAX
THICKNESS(MM) C Mn Si P S N Cu
≦40 0.18 1.5 ~ 0.025 0.025 0.012 0.55
>40 0.18
Mechanical properties MIN
  Yield Strength MPa Tensile Strength MPa Elongation in 2 in. %
≦16 275 410-580 13
>16,  ≦100 235
>100 195 410-580
EN10025-2 S275J0
Chemical composition % MAX
THICKNESS(MM) C Mn Si P S N Cu
≦40 0.18 1.5 ~ 0.03 0.03 0.012 0.55
>40 0.18
Mechanical properties MIN
  Yield Strength MPa Tensile Strength MPa Elongation in 2 in. %
≦16 275 410-580 15
>16,  ≦100 235
>100 205 380-540
EN10025-2 S355J0
Chemical composition % MAX
THICKNESS(MM) C Mn Si P S N Cu
≦40 0.20 1.6 0.55 0.03 0.03 0.012 0.55
>40 0.22
Mechanical properties MIN
  Yield Strength MPa Tensile Strength MPa Elongation in 2 in. %
≦16 355 470-680 14
>16,  ≦100 315
>100 275 450-600
EN10025-2 S355JR
Chemical composition % MAX
THICKNESS(MM) C Mn Si P S N Cu
≦40 0.24 1.6 0.55 0.035 0.035 0.012 0.55
>40 0.24
Mechanical properties MIN
  Yield Strength MPa Tensile Strength MPa Elongation in 2 in. %
≦16 355 470-680 14
>16,  ≦100 315
>100 275 450-600
EN10025-2 S355K2
Chemical composition % MAX
THICKNESS(MM) C Mn Si P S N Cu
≦40 0.20 1.6 0.55 0.025 0.025 ~ 0.55
>40 0.22
Mechanical properties MIN
  Yield Strength MPa Tensile Strength MPa Elongation in 2 in. %
≦16 355 470-680 12
>16,  ≦100 315
>100 265 450-600
EN10025-2 S355J2
Chemical composition % MAX
THICKNESS(MM) C Mn Si P S N Cu
≦40 0.20 1.6 0.55 0.025 0.025 ~ 0.55
>40 0.22
Mechanical properties MIN
  Yield Strength MPa Tensile Strength MPa Elongation in 2 in. %
≦16 355 470-680 14
>16,  ≦100 315
>100 265 450-600
EN10025-2 S420J0
Chemical composition % MAX
THICKNESS(MM) C Mn Si P S N Cu
≦40 0.20 1.7 0.55 0.03 0.03 0.025 0.55
>40 0.22
Mechanical properties MIN
  Yield Strength MPa Tensile Strength MPa Elongation in 2 in. %
≦16 450 550-720 17
>16,  ≦100 410
>100 380 530-700

If you are interested in other carbon steel plates, please click here - ASTM A36, ASTM A283, ASTM A572, ASTM A656, JIS G3101 SS400, DIN 17100, DIN 17102, GB/T700, GB/T1591